Preparation and Properties of Bilayer Composite Materials of Cu-coated Fe and CuSn10

YEXuan (Mechanical and Electrical Engineering College, Heyuan Polytechnic), QINLing (R&D Department, Heyuan Peak metal products Co., Ltd.), LINGYuxiang (R&D Department, Heyuan Yueao Cemented Carbide Co., Ltd.)

Abstract


Bilayer composite materials of Cu-coated Fe and CuSn10 containing 0%, 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50% Cu-coated Fe were prepared in mesh belt sintering furnace. Microscopic pore morphology of materials was observed, bending strength was tested. Results show that, There is a good bonding between Cu-coated Fe and CuSn10, with the increase of Cu-coated Fe content from 0% to 50%, bending strength of bilayer composite materials increases.

Keywords


Cu-coated Fe; CuSn10; bilayer composite

Full Text:

PDF

References


LI Dongyu, LI Xiaoqiang, LI Jingmao, et al.. Effect of Sintering Process on Microstructure and Properties of Copper-Iron-based Oil-impregnated Bearing[J]. Materials Reports, 2021,35(8):8157-8163.

HUANG Zhao-xuan, LAN Jiang, YANG Shi-yu, et al.. Effect of MoS2 and graphite on friction properties of bronze oil bearing[J]. Powder Metallurgy Technology, 2020,38(5):363-370.

YE Xuan, TU Huajin, QIN Ling, et al.. Properties of Fe-Cu-C composite reinforced by different WC content[J]. IOP Conference Series: Materials Science and Engineering, 2019, 688(3):109-112.

YE Xuan, QIN Ling. Preparation and performance of WC/TiC reinforced iron matrix composites[J]. Powder Metallurgy Industry, 2021,31(4):49-54.

YE Xuan, TU Huajin, QIU Zhiwen, et al.. Effects of WC Content on Pore Morphology and Properties of Fe-1.5Cu-1.8Ni-0.5Mo-1C PM Composite[J]. Hot Working Technology, 2019,48(22): 89-93.

YE Xuan, TU Huajin, QIU Zhiwen, et al.. Effect of WC particle reinforcement on Fe–1.5Cu–1.8Ni–0.5Mo–1C P/M composite[J]. Powder Metallurgy Technology, 2019,37(1):40-45.

WANG Jingxuan, WANG Jiaqi, YIN Yanguo, et al.. Dry Friction Characteristics of FeS/Cu-Bi Copper-Based Sliding Bearing Materials[J]. Bearing, 2020(3):39-43.

ZHANG Shanshan, LI Changyun, PAN Yuewu, et al.. Application and preparation of copper-coated iron powders[J]. Powder Metallurgy Technology, 2020,38(6):465-474.

Yang Lei, Gao Qiu, Liu Hong, et al.. Fabrication and Properties of Dual-Gradient Nanostructured Copper Matrix Composites Reinforced by Silicon Carbide Particles[J]. Powder Metallurgy Technology, 2016,34(6):428-433.




DOI: https://doi.org/10.33142/rams.v5i2.12709

Refbacks

  • There are currently no refbacks.


Copyright (c) 2024 Xuan YE, Ling QIN, Yuxiang LING

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.