Effect of Carbides and γ/γ' Eutectic on Crack Initiation and Propagation in Ni-based Superalloy

QINJunwei, CHENXiaohua, CHENKaixuan, YANGXinghai, XIEWeiyang, WANGYanlin, WANGZidong

Abstract


The Ni-based Udemit720Li superalloy tends to form large γ/γ' eutectic on grain boundaries (GBs) during solidification due to the addition of excessive Al and Ti elements, which provides convenience to study the effect of carbide and γ/γ' eutectic on crack initiation and propagation during tensile process. In this paper, Udemit720Li superalloy samples were prepared by induction melting casting method, arc melting and suction casting method. The microstructure, tensile properties and mechanism of crack initiation and propagation in Ni-based superalloy fabricated by two methods are investigated. The results exhibit γ/γ' eutectic accelerates the stress concentration at GB and thus leads to premature fracture failure. The samples with grain-boundary eutectic have higher strain hardening rate, but their cumulative and local misorientations are lower. For samples without eutectic at GB, the primary crack initiates at grain-boundary carbide along GB and extends along GB or into grain matrix, and exhibits better deformation performance and dislocation storage capacity within grains.


Keywords


Superalloy; Carbides; Eutectic; Crack

Full Text:

PDF

References


Kim S E, Jackson M P, Reed R C, et al. Quantification of the minor precipitates in UDIMET™ alloy720(LI) using electrolytic extraction and X-ray diffraction 1[J]. Materials Science & Engineering A, 1998, 245(2):225-232.

Yongchang L, Qianying G, Chong L I, et al. Recent progress on evolution of precipitates in Inconel 718 superalloy [J]. Acta Metallurgica Sinica, 2016.

Mao J, Chang K M, Yang W, et al. Cooling precipitation and strengthening study in powder metallurgy superalloy U720LI[J]. Metallurgical & Materials Transactions A, 2001, 32(10):2441-2452.

F E Sczerzenie, G E Maurer. Development of Udimet 720 for High Strength Disk Applications[J]. Special Metals Corporation, 1984

P W Keefe, S O Mancuso, G E Maurer. Effect of heat treatment and chemistry on the long-term phase stability of a high strength nickel-based superalloy[J]. Superalloys, 1992, 487-496

Bain K R, Gambone M L, Hyzak J M, et al. Development of Damage Tolerant Microstructures in Udimet 720[C]// Superalloys. 1988.

Na Y S, Park N K, Reed R C. Sigma morphology and precipitation mechanism in udimet 720Li[J]. Scripta Materialia, 2000, 43(7):585-590.

Zhao G D, Yu L X, Qi F, et al. The Minor Precipitation at the Final Stage of U720Li Solidification[J]. Acta Metallurgica Sinica, 2016, 29(6):518-526.

Li F, Fu R, Yin F, et al. Impact of γ'(Ni3(Al,Ti)) phase on dynamic recrystallization of a Ni-based disk superalloy during isothermal compression[J]. Journal of Alloys & Compounds, 2017, 693:1076-1082.

Joseph C, Persson C, Colliander M H. Influence of heat treatment on the microstructure and tensile properties of Ni-base superalloy Haynes 282[J]. Materials Science and Engineering: A, 2016:S0921509316312618.

Liu F, Chen J, Dong J, et al. The hot deformation behaviors of coarse, fine and mixed grain for Udimet 720Li superalloy[J]. Materials Science and Engineering: A, 2016, 651:102-115.

Du B, Sheng L, Cui C, et al. Precipitation and evolution of grain boundary boride in a nickel-based superalloy during thermal exposure[J]. Materials Characterization, 2017, 128:109-114.

Osada T, Gu Y, Nagashima N, et al. Optimum microstructure combination for maximizing tensile strength in a polycrystalline superalloy with a two-phase structure[J]. Acta Materialia, 2013, 61(5):1820-1829.

Yan B C, Zhang J, Lou L H. Effect of boron additions on the microstructure and transverse properties of a directionally solidified superalloy[J]. Materials Science & Engineering A, 2008, 474(1-2):39-47.

Chang L, Jin H, Sun W. Solidification Behavior of Ni-base Superalloy Udimet 720Li[J]. Journal of Alloys & Compounds, 2015.

Pang H T, Reed P A S. Effects of microstructure on room temperature fatigue crack initiation and short crack propagation in Udimet 720Li Ni-base superalloy[J]. International Journal of Fatigue, 2008, 30(10-11):2009-2020.

Zhipeng W, Lianxi H, Yu S, et al. Effect of solution treatment on microstructure and tensile properties of a U720LI Ni-based superalloy[J]. Vacuum, 2018, 156: 248-255

Villechaise P, Cormier J, Billot T, et al. Mechanical Behavior and Damage Processes of Udimet 720Li: Influence of Localized Plasticity at Grain Boundaries[M]// Superalloys 2012.

Rao G A, Satyanarayana D V V. Influence of HIP processing on microstructure and mechanical properties of superalloy Udimet 720LI[J]. Materials Science & Technology.

Lu K. The Future of Metals[J]. Science, 2010, 328:319-320.

M. A. Meyers, A. Mishra, D.J. Benson, Mechanical properties of nanocrystalline materials, Progress in Materials Science. 51: 427-556.

Lu K. Stabilizing nanostructures in metals using grain and twin boundary architectures[J]. Nature Reviews Materials, 2016, 1(5):16019.

Valiev R Z. Nanostructured alloys: Large tensile elongation[J]. Nature Materials, 2013, 12(4):289-291.

Liu G, Zhang G J, Jiang F, et al. Nanostructured high-strength molybdenum alloys with unprecedented tensile ductility[J]. Nature Materials, 2013, 12(4):344-350.

Launey M E, Ritchie R O. On the Fracture Toughness of Advanced Materials[J]. Advanced Materials, 2009, 21(21):2103-2110.

Kaixuan C, Xiaohua C, Zidong W, et al. Optimization of deformation properties in as-cast copper by microstructural engineering. Part I. microstructure[J]. Journal of Alloys and Compounds, 2018, 763:592-605.

Lu K, Lu L, Suresh S. Strengthening Materials by Engineering Coherent Internal Boundaries at the Nanoscale[J]. SCIENCE, 2009, 324(5925):349-352.

Chen K X, Chen X H, Ding D, et al. Effect of in-situ nanoparticle wall on inhibiting segregation of tin bronze alloy[J]. Materials Letters, 2016, 175:148-151.

Seo S M, Lee J H, Yoo Y S, et al. A Comparative Study of theγ/γ'Eutectic Evolution During the Solidification of Ni-Base Superalloys[J]. Metallurgical & Materials Transactions A, 2011, 42(10):3150-3159.

Bingming G, Lin L, Xinbao Z, et al. Effect of Directional Solidification Methods on the Cast Microstructure and Grain Orientation of Blade Shaped DZ125 Superalloy[J]. Rare Metal Materials and Engineering, 2013, 42(11):2222-2227.

Liu L, Huang T W, Zhang J, et al. Microstructure and stress rupture properties of single crystal superalloy CMSX-2 under high thermal gradient directional solidification[J]. Materials Letters, 2007, 61(1):227-230.

Seo S M, Lee J H, Yoo Y S, et al. A Comparative Study of the γ/γ' Eutectic Evolution During the Solidification of Ni-Base Superalloys[J]. Metallurgical & Materials Transactions A, 2011, 42(10):3150-3159.

Wang Q, Ding H, Zhang H, et al. Variations of microstructure and tensile property of γ-TiAl alloys with 0~0.5 at% C additives[J]. Materials Science and Engineering A, 2017, 700:198-208.

Kuhn F, Zeismann F, Brueckner-Foit A. Crack growth mechanisms in an aged superalloy at high temperature[J]. International Journal of Fatigue, 2014, 65:86-92.

Miao J, Pollock T M, Jones J W. Microstructural Extremes and the Transition from Fatigue Crack Initiation to Small Crack Growth in a Polycrystalline Nickel-base Superalloy[J]. Acta Materialia, 2012, 60(s 6–7):2840–2854.

Jiashi Miao, Tresa M Pollock, J Wayne Jones. Crystallographic fatigue crack initiation in nickel-based superalloy René 88DT at elevated temperature[J]. Acta materialia, 2009, 5946-5974

Randle V , Hansen N , Jensen D J . The deformation behaviour of grain boundary regions in polycrystalline aluminium[J]. Philosophical Magazine A, 1996, 73(2):265-282.




DOI: https://doi.org/10.33142/rams.v2i2.3170

Refbacks

  • There are currently no refbacks.


Copyright (c) 2020 Junwei QIN, Xiaohua CHEN, Kaixuan CHEN, Xinghai YANG, Weiyang XIE, Yanlin WANG, Zidong WANG

Creative Commons License
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.